The Kinetics of the Glass Transition and Physical Aging in Germanium Selenide Glasses

Haoyu Zhao, Yungpyo Koh, Marek Pyda, Sabyasachi Sen, Sindee Simon

Research output: Contribution to journalArticlepeer-review

Abstract

The kinetics associated with the glass transition is investigated using differential scanning calorimetry (DSC) for germanium selenide glasses with Ge content ranging from 0 to 30 at.% and average coordination numbers ranging from 2.0 to 2.6. As Ge content increases, the glass transition region broadens and the step change in heat capacity at Tg decreases. As a result of physical aging, enthalpy overshoots are observed in DSC heating scans and the corresponding change in enthalpy can be calculated as a function of aging time. The change in enthalpy linearly increases with the logarithm of aging time and then levels off at an equilibrium value that increases with decreasing aging temperature. The time required to reach equilibrium increases with decreasing aging temperature and, at a given distance from Tg, the time increases with decreasing germanium content. The results indicate that all samples show expected physical aging behavior, and no evidence is found for a Boolchand intermedi
Original languageEnglish
Pages (from-to)63-70
JournalJournal of Non-Crystalline Solids
DOIs
StatePublished - Apr 2013

Fingerprint Dive into the research topics of 'The Kinetics of the Glass Transition and Physical Aging in Germanium Selenide Glasses'. Together they form a unique fingerprint.

Cite this