PolyDODT: A macrocyclic elastomer with unusual properties

Kristof Molnar, Hojin Kim, Dongjie Chen, Carin A. Helfer, Gabor Kaszas, Gregory B. McKenna, Julia A. Kornfield, Chunhua Yuan, Judit E. Puskas

Research output: Contribution to journalArticlepeer-review

1 Scopus citations

Abstract

The effect of reaction conditions on the structure of poly(3,6-dioxa-1,8-octanedithiol) (polyDODT) made by Reversible Radical Recombination Polymerization (R3P) using triethylamine (TEA), H2O2 and air was investigated. 800 MHz (1 and 2D) NMR was used to investigate the polymer structures. Sensitivity analysis provided direct evidence for high purity cyclic polyDODT up to Mn ∼ 100 000 g mol-1. Comparative analysis by High Resolution Multidetector Size Exclusion Chromatography (SEC) using integrated data showed that the cycles had lower viscosity and were more compact (both for Rg and Rh) than linear samples of similar molecular weight. However, differential data revealed unusual behavior. While lower molecular weight cyclic polymers eluted later and had lower intrinsic viscosity than their linear counterparts at the same molecular weight, at higher molecular weights the polymers showed strange behavior: both the diffusion coefficient measured by Quasielastic Light Scattering (QELS) and Mark-Houwink-Sakurada plots of intrinsic viscosity for linear and cyclic polyDODT were found to converge. R3P, an aqueous based "green"method is capable of producing polymers at the 10-100 g scale in the lab, which will allow more detailed studies of this new class of biodegradable elastomers so further experimentation can be performed to elucidate the reasons for the unusual findings. This journal is

Original languageEnglish
Pages (from-to)668-676
Number of pages9
JournalPolymer Chemistry
Volume13
Issue number5
DOIs
StatePublished - Feb 7 2022

Fingerprint

Dive into the research topics of 'PolyDODT: A macrocyclic elastomer with unusual properties'. Together they form a unique fingerprint.

Cite this