Effect of surface coating and tin plating on friction characteristics of P-110 tubing for different thread compounds

O. Cuvalci; I. Cicek; A. Ertas

Effect of surface coating and tin plating on friction characteristics of P-110 tubing for different thread compounds

O. Cuvalci, I. Cicek, A. Ertas

Mechanical Engineering

Research output: Contribution to conference › Paper › peer-review

Abstract

This paper presents the results of an experimental study conducted to determine friction coefficient of coated with manganese phosphate (pin and bax) and tin plated (box) P-110 tubing with API modified Threadkote 706, Shell Type 3 and Graphite/PTFE thread compounds. The surface roughness of the specimens was nominally 50 μin. Six repeated tests were run at a rotational speed of 5 rpm. In each test the bearing load was increased monotonically to a maximum of 625 kN. Friction coefficient data obtained during the tests are presented and discussed.

Original language	English
State	Published - 1999
Event	Proceedings of the 1999 ASME Energy Sources Technology Conference - Houston, TX, USA Duration: Feb 1 1999 → Feb 3 1999

Conference

Conference	Proceedings of the 1999 ASME Energy Sources Technology Conference
City	Houston, TX, USA
Period	02/1/99 → 02/3/99

Cite this

@conference{b581fb4873c543d6872c8b2ae226c2ee,

title = "Effect of surface coating and tin plating on friction characteristics of P-110 tubing for different thread compounds",

abstract = "This paper presents the results of an experimental study conducted to determine friction coefficient of coated with manganese phosphate (pin and bax) and tin plated (box) P-110 tubing with API modified Threadkote 706, Shell Type 3 and Graphite/PTFE thread compounds. The surface roughness of the specimens was nominally 50 μin. Six repeated tests were run at a rotational speed of 5 rpm. In each test the bearing load was increased monotonically to a maximum of 625 kN. Friction coefficient data obtained during the tests are presented and discussed.",

author = "O. Cuvalci and I. Cicek and A. Ertas",

year = "1999",

language = "English",

note = "Proceedings of the 1999 ASME Energy Sources Technology Conference ; Conference date: 01-02-1999 Through 03-02-1999",

}

TY - CONF

T1 - Effect of surface coating and tin plating on friction characteristics of P-110 tubing for different thread compounds

AU - Cuvalci, O.

AU - Cicek, I.

AU - Ertas, A.

PY - 1999

Y1 - 1999

N2 - This paper presents the results of an experimental study conducted to determine friction coefficient of coated with manganese phosphate (pin and bax) and tin plated (box) P-110 tubing with API modified Threadkote 706, Shell Type 3 and Graphite/PTFE thread compounds. The surface roughness of the specimens was nominally 50 μin. Six repeated tests were run at a rotational speed of 5 rpm. In each test the bearing load was increased monotonically to a maximum of 625 kN. Friction coefficient data obtained during the tests are presented and discussed.

AB - This paper presents the results of an experimental study conducted to determine friction coefficient of coated with manganese phosphate (pin and bax) and tin plated (box) P-110 tubing with API modified Threadkote 706, Shell Type 3 and Graphite/PTFE thread compounds. The surface roughness of the specimens was nominally 50 μin. Six repeated tests were run at a rotational speed of 5 rpm. In each test the bearing load was increased monotonically to a maximum of 625 kN. Friction coefficient data obtained during the tests are presented and discussed.

UR - http://www.scopus.com/inward/record.url?scp=0032657301&partnerID=8YFLogxK

M3 - Paper

AN - SCOPUS:0032657301

T2 - Proceedings of the 1999 ASME Energy Sources Technology Conference

Y2 - 1 February 1999 through 3 February 1999

ER -

Effect of surface coating and tin plating on friction characteristics of P-110 tubing for different thread compounds

Abstract

Conference

Other files and links

Fingerprint

Cite this