T1 - Correlation between sheet carrier density-mobility product and persistent photoconductivity in AlGaN/GaN modulation doped heterostructures
AU - Li, J. Z.
AU - Li, J.
AU - Lin, J. Y.
AU - Jiang, H. X.
N1 - Funding Information:
This research is supported by BMDO (Dr. Kepi Wu) monitored by USASSDC, NSF (DMR-99502431), and DOE(DE-FG03-96ER45604).
PY - 2000
Y1 - 2000
N2 - High quality Al0.25Ga0.75N/GaN modulation-doped heterojunction field-effect transistor (MOD-HFET) structures grown on sapphire substrates with high sheet carrier density and mobility products (nsμ > 1016/Vs at room temperature) have been grown by metal organic chemical vapor deposition (MOCVD). The optimized structures were achieved by varying structural parameters, including the AlGaN spacer layer thickness, the Si-doped AlGaN barrier layer thickness, the Si-doping concentration, and the growth pressure. In these structures, the persistent photoconductivity (PPC) effect associated with the two-dimensional electron gas (2DEG) system was invariantly observed. As a consequence, the characteristic parameters of the 2DEG were sensitive to light and the sensitivity was associated with permanent photoinduced increases in the 2DEG carrier mobility (μ) and sheet carrier density (ns). However, we observed that the magnitude of the PPC and hence the photoinduced instability associated with these heterostructures were a strong function of only one parameter, the product of ns and μ, which is the most important parameter for the HFET device design. For a fixed excitation photon dose, the ratio of the low temperature PPC to the dark conductivity level was observed to decrease from 200% to 3% as the nsμ (300 K) product was increased from 0.048 × 1016/Vs to 1.4 × 1016/Vs. Based on our studies, we suggest that the magnitude of the low temperature PPC can be used as a sensitive probe for monitoring the electronic quality of the AlGaN/GaN HFET structures.
AB - High quality Al0.25Ga0.75N/GaN modulation-doped heterojunction field-effect transistor (MOD-HFET) structures grown on sapphire substrates with high sheet carrier density and mobility products (nsμ > 1016/Vs at room temperature) have been grown by metal organic chemical vapor deposition (MOCVD). The optimized structures were achieved by varying structural parameters, including the AlGaN spacer layer thickness, the Si-doped AlGaN barrier layer thickness, the Si-doping concentration, and the growth pressure. In these structures, the persistent photoconductivity (PPC) effect associated with the two-dimensional electron gas (2DEG) system was invariantly observed. As a consequence, the characteristic parameters of the 2DEG were sensitive to light and the sensitivity was associated with permanent photoinduced increases in the 2DEG carrier mobility (μ) and sheet carrier density (ns). However, we observed that the magnitude of the PPC and hence the photoinduced instability associated with these heterostructures were a strong function of only one parameter, the product of ns and μ, which is the most important parameter for the HFET device design. For a fixed excitation photon dose, the ratio of the low temperature PPC to the dark conductivity level was observed to decrease from 200% to 3% as the nsμ (300 K) product was increased from 0.048 × 1016/Vs to 1.4 × 1016/Vs. Based on our studies, we suggest that the magnitude of the low temperature PPC can be used as a sensitive probe for monitoring the electronic quality of the AlGaN/GaN HFET structures.
UR - http://www.scopus.com/inward/record.url?scp=0033702366&partnerID=8YFLogxK
M3 - Conference article
AN - SCOPUS:0033702366
SN - 0272-9172
VL - 595
SP - W11.12.1 - W11.12.6
JO - Materials Research Society Symposium - Proceedings
JF - Materials Research Society Symposium - Proceedings
T2 - The 1999 MRS Fall Meeting - Symposium W 'GaN and Related Alloys'
Y2 - 28 November 1999 through 3 December 1999
ER -